Comparison table for material of tooling and mould
¡ôReference for general material of tooling and mould.
Reference of general
material from LZQ
Hardness Bending strength Compression strength Density
HV30 HRA N/mm2 psi N/mm2 psi g/cm3
H10F 1600 92.1 3750 - 6300 - 14.50
H10F-1 1600 92.1 4300 623000 6250 906250 14.45
DK20 1500 91.4 2300 - 5300 - 14.70
DZ05 1900 93.8 2300 - 7700 - 15.00
DZ05 1900 93.8 2300 333000 6900 1000000 15.00
H3M 1750 93.0 1900 - 6900 - 15.20
H4M 1750 93.0 2000 290000 6900 1000000 1500
H5M 1700 92.7 2100 - 6700 - 15.00
H5M 1700 92.8 2100 305000 6700 971000 14.95
H6N 1575 91.9 2200 319000 6200 899000 14.95
H10N 1400 90.4 2600 - 5200 - 14.60
H12N 1300 89.3 2800 - 4600 - 14.30
DA25 1450 90.9 2400 348000 5200 754000 14.65
DC03 1900 93.8 2100 305000 7500 1088000 15.25
DZ05 1900 93.8 2300 333000 6900 1000000 15.00
H3F 1925 93.9 2200 319000 7800 1131000 15.25
H15F 1400 90.4 4000 580000 - - 13.95
DH10 1720 92.9 2300 333000 - - 15.00
¡ôApproximate comparison table for material of diamond tungsten steel kind G.
ISO LZQ Germany France Japan Russia Sweden England America
LZQ Diamond DIN Widia Unit Tykram Carbex Jls Lgetalloy §¤OCT Sandvik
Coromant
Seco BHMA Wimet Annolloy JlC Wendt-Sonis Kennametal
G05 NUA61
KU301Z
G6 - GT05 G05
B10
- G10 - G10E BK6 CS10
CS20
- - NH
N
F1/F - - -
G10 KUA720
KU301Z
G6 G1 GT10 G10 TG1 G12 E1 G2 BK6B CS20 - - X12 F1/C - - -
G15 PUA71 G8 - GT15 G15
B30
TG2 E4 - G3 BK8B CG35
CS40
- - CT
90B
F2/8C - - -
G20 PUA181 G11 G2 GT20
GT40
G20
G40
TG3 E5 E2 G5 BK10 CG40 - - G
R11
110B
F2/10C - - -
G30 VUA221Z G15 G3 GT30
GT50
G30
B50
TG4 E6 E3 G6 BK15 CG60
CT50
- - BP1 F2/15C - - -
G40 VUA324
VUA351
- G4 GT40 G40 TG5 G40 E4 G7 BK20 - - - - F2/20C - - -
G50 VUA421 - G5 GT50 G50 TG6 G50 E5 G8 BK25 CT70
CT80
- - TT F2/25C - - -
G60 VUA521 - G6 GT60 G60 - - - - BK30 - - - - F2/30C - - -